Yttrium iron molybdenum nitride (1/10.1/1.9/0.8)

Fe_10.12Mo_1.88N_0.8Y

Tomey, E Isnard, O Fagan, A Desmoulins, C Miraglia, S Soubeyroux, J L Fruchart, D

Journal of Alloys Compd. (1993) 191, 233-238

a=8.6590(8)Å b=8.6590(8)Å c=4.7930(5)Å

α=90° β=90° γ=90°

Neodymium iron molybdenum nitride (1/10.5/1.5/0.8)

Fe_10.52Mo_1.48N_0.8Nd

Tomey, E Isnard, O Fagan, A Desmoulins, C Miraglia, S Soubeyroux, J L Fruchart, D

Journal of Alloys Compd. (1993) 191, 233-238

a=8.6398(9)Å b=8.6398(9)Å c=4.8437(6)Å

α=90° β=90° γ=90°

Neodymium iron molybdenum nitride (1/10.5/1.5/0.8)

Fe_10.48Mo_1.52N_0.8Nd

Tomey, E Isnard, O Fagan, A Desmoulins, C Miraglia, S Soubeyroux, J L Fruchart, D

Journal of Alloys Compd. (1993) 191, 233-238

a=8.646(1)Å b=8.646(1)Å c=4.8519(6)Å

α=90° β=90° γ=90°

Samarium cobalt silicon carbide (1/9/2/0.6)

C_0.6Co₉Si₂Sm

Skolozdra, R Akselrud, L Fruchart, D Gignoux, D Gorolenko, Yu Soubeyroux, J L Tomey, E

Journal of Magnetism and Magnetic Materials (1995) 140, 915-916

a=9.838Å b=9.838Å c=6.377Å

α=90° β=90° γ=90°

Yttrium iron titanium deuteride (2/17.2/2.3/2.4)

D_2.35Fe_17.17Ti_2.28Y₂

Revel, R Tomey, E Soubeyroux, J L Fruchart, D Jacobs, T H Buschow, K H J

Journal of Alloys Compd. (1993) 202, 57-61

a=8.276(1)Å b=8.276(1)Å c=4.820(1)Å

α=90° β=90° γ=90°

Fe_17.2Ti_2.38Y₂

Revel, R.Tomey, E.Fruchart, D.Soubeyroux, J.L.Buschow, K.H.J.Jacobs, T.H.

Journal of Alloys Compd. (1993) 202, 57-61

a=8.209Å b=8.209Å c=4.814Å

α=90° β=90° γ=90°

Fe_10.2Mo_1.8Nd

Tomey, E.Fagan, A.Isnard, O.Fruchart, D.Desmoulins, C.Soubeyroux, J.L.Miraglia, S.

Journal of Alloys Compd. (1993) 191, 233-238

a=8.5952Å b=8.5952Å c=4.7908Å

α=90° β=90° γ=90°

Fe_10.4Mo_1.6Y

Tomey, E.Isnard, O.Desmoulins, C.Fruchart, D.Fagan, A.Miraglia, S.Soubeyroux, J.L.

Journal of Alloys Compd. (1993) 191, 233-238

a=8.5336Å b=8.5336Å c=4.782Å

α=90° β=90° γ=90°

Yttrium iron molybdenum nitride (1/10.1/1.9/0.8)

Fe_10.12Mo_1.88N_0.8Y

Tomey, E Isnard, O Fagan, A Desmoulins, C Miraglia, S Soubeyroux, J L Fruchart, D

Journal of Alloys Compd. (1993) 191, 233-238

a=8.6648(6)Å b=8.6648(6)Å c=4.8012(5)Å

α=90° β=90° γ=90°